Pengaruh Quenching dan Media Pendingin terhadap sifat Fisis dan Mekanis Baja Paduan Fe97,99mn1,60c0,41

Budiarto, Budiarto and Turnip, Kimar (2015) Pengaruh Quenching dan Media Pendingin terhadap sifat Fisis dan Mekanis Baja Paduan Fe97,99mn1,60c0,41. Teknoin, 21 (4). pp. 191-199. ISSN 0853 8697

[img]
Preview
Text
teknoin.compressed.pdf

Download (1MB) | Preview
Official URL: http://repo.uki.ac.id

Abstract

The mechanical properties of Fe97,91Mn1,60C0,41 steel alloy have improved, especially hardness after been subjected to various quenching media. Samples were heated at austenite temperature 800oC and 2 hours holding time, then quenched in water, oil, and salt water. The microstructures obtained were used to explain the results using optical microscope. Crystal structure and hardness were studied using X-Ray Diffractometer and Brinell Hardness Test. The hardness values of the quenched samples were 375 HB in salt water media, 257 HB in water media, and 231 HB in oil media. Crystal transformation from FCC -austenit to BCT α-martensit were observed in optical microscope and 2 peak values of XRD test result.

Item Type: Article
Subjects: TECHNOLOGY > Chemical technology
Depositing User: Mr. Admin Repository
Date Deposited: 23 Oct 2018 03:01
Last Modified: 16 Jul 2021 15:27
URI: http://repository.uki.ac.id/id/eprint/324

Actions (login required)

View Item View Item