Murti, Danang Wisnu Murti (2025) Pengaruh Jenis Kawat Las Terhadap Kekuatan Sambungan Las Pada Cetakan Yang Menggunakan Material S45C. S1 thesis, Universitas Kristen Indonesia.
This is the latest version of this item.
![[img]](http://repository.uki.ac.id/style/images/fileicons/text.png) |
Text (Hal_Judul_Daftar_Isi_Daftar_Gambar_Daftar_Tabel_Daftar_Singkatan_Abstrak)
HalJudulDaftarIsiDaftarGambarDaftarTabelDaftarSingkatanAbstrak.pdf Available under License Creative Commons Attribution Non-commercial Share Alike. Download (7MB) |
|
Text (BAB_I)
BABI.pdf Available under License Creative Commons Attribution Non-commercial Share Alike. Download (3MB) |
|
Text (BAB_II)
BABII.pdf Restricted to Registered users only Available under License Creative Commons Attribution Non-commercial Share Alike. Download (9MB) |
|
Text (BAB_III)
BABIII.pdf Restricted to Registered users only Available under License Creative Commons Attribution Non-commercial Share Alike. Download (7MB) |
|
Text (BAB_IV)
BABIV.pdf Restricted to Registered users only Available under License Creative Commons Attribution Non-commercial Share Alike. Download (8MB) |
|
Text (BAB_V)
BABV.pdf Restricted to Registered users only Available under License Creative Commons Attribution Non-commercial Share Alike. Download (847kB) |
|
Text (DAFTAR_PUSTAKA)
DAFTARPUSTAKA.pdf Available under License Creative Commons Attribution Non-commercial Share Alike. Download (1MB) |
|
Text (LAMPIRAN)
LAMPIRAN.pdf Restricted to Repository staff only Available under License Creative Commons Attribution Non-commercial Share Alike. Download (205kB) |
Abstract
Penelitian ini bertujuan untuk menganalisis pengaruh jenis kawat las terhadap kekuatan sambungan las pada cetakan yang menggunakan material baja karbon sedang tipe S45C. Material ini banyak digunakan dalam industri manufaktur, khususnya pada pembuatan cetakan untuk produk berbahan PVC yang menjadi sandal. Permasalahan utama dalam penelitian ini adalah bagaimana jenis kawat las yang berbeda memengaruhi hasil pengelasan, baik dari segi kekerasan, kekuatan tarik, maupun struktur mikro pada area sambungan. Tiga jenis kawat las yang digunakan yaitu E6013, E7016, dan E7018, masing-masing memiliki karakteristik fluks dan komposisi berbeda yang dapat memengaruhi hasil pengelasan. Penelitian ini dilakukan secara eksperimental dengan proses pengelasan menggunakan metode Shielded Metal Arc Welding (SMAW) pada pelat baja S45C, kemudian dilanjutkan dengan pengujian kekerasan Rockwell C, uji tarik, serta pengamatan struktur mikro menggunakan mikroskop optik pada tiga zona utama yaitu Base Metal, Heat Affected Zone (HAZ), dan Weld Metal (WM). Hasil uji menunjukkan bahwa elektroda E7018 menghasilkan kekerasan tertinggi pada weld metal (17,67 HRC) dan HAZ (24,87 HRC). Elektroda E7018 menghasilkan kekuatan tarik terbesar yaitu 87,40 Kgf/mm2, menunjukkan struktur mikro dengan fasa perlit dan ferrit yang rapat. E7016 berada di tengah dengan nilai kekerasan weld metal (15,93 HRC) dan HAZ (24,66 HRC). Dan menghasilkan kekuatan tarik 77,61Kgf/mm2, sedangkan E6013 menunjukkan kekerasan terendah, terutama pada logam las (10,30 HRC) dengan hasil uji tarik sebesar 71,99 Kgf/mm2, yang mengindikasikan struktur mikro yang lebih lunak dan kurang padat. Kesimpulan dari penelitian ini adalah bahwa pemilihan jenis elektroda sangat berpengaruh terhadap hasil pengelasan, dan E7018 menjadi kawat las yang menghasilan kekuatan tarik dan kekerasan paling tinggi pada penelitian ini untuk material S45C. Kata Kunci: S45C, kawat las E6013, E7016, E7018, SMAW, kekerasan HRC, struktur mikro, sambungan las./ This study aims to analyze the effect of welding electrode type on the strength of welded joints in molds made from medium carbon steel S45C. This material is widely used in manufacturing industries, particularly for producing molds for PVC-based products such as sandals. The main problem addressed in this research is how different types of welding electrodes influence the welding results in terms of hardness, tensile strength, and microstructural characteristics of the joint area. Three types of electrodes were employed: E6013, E7016, and E7018, each with distinct flux compositions and chemical characteristics that can affect welding outcomes. The research was conducted experimentally using the Shielded Metal Arc Welding (SMAW) process on S45C steel plates, followed by Rockwell C hardness testing, tensile testing, and microstructural observation with an optical microscope across three main zones: Base Metal, Heat Affected Zone (HAZ), and Weld Metal (WM). The test results showed that the E7018 electrode produced the highest hardness in the weld metal (17.67 HRC) and HAZ (24.87 HRC). E7018 also achieved the highest tensile strength of 87,40 Kgf/mm², displaying a microstructure with dense pearlite and ferrite phases. E7016 ranked intermediate, with weld metal hardness of 15.93 HRC, HAZ hardness of 24.66 HRC, and tensile strength of 77,61 Kgf/mm². In contrast, E6013 exhibited the lowest hardness, especially in the weld metal (10.30 HRC), and the lowest tensile strength of 71,99 Kgf/mm², indicating a softer and less compact microstructure. The study concludes that the selection of electrode type significantly affects welding results, with E7018 being the electrode that produces the highest tensile strength and hardness in this research for S45C steel material. Keywords: S45C, E6013 welding electrode, E7016, E7018, SMAW, HRC hardness, microstructure, weld joint.
| Item Type: | Thesis (S1) | ||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Contributors: |
|
||||||||||||
| Subjects: | TECHNOLOGY > Mechanical engineering and machinery | ||||||||||||
| Divisions: | FAKULTAS TEKNIK > Teknik Mesin | ||||||||||||
| Depositing User: | Mr Danang Wisnu Murti | ||||||||||||
| Date Deposited: | 26 Sep 2025 09:35 | ||||||||||||
| Last Modified: | 26 Sep 2025 09:35 | ||||||||||||
| URI: | http://repository.uki.ac.id/id/eprint/20632 |
Available Versions of this Item
-
Pengaruh Jenis Kawat Las Terhadap Kekuatan Sambungan Las Pada Cetakan Yang Menggunakan Material S45C. (deposited 19 Sep 2025 08:15)
- Pengaruh Jenis Kawat Las Terhadap Kekuatan Sambungan Las Pada Cetakan Yang Menggunakan Material S45C. (deposited 26 Sep 2025 09:35) [Currently Displayed]
Actions (login required)
 |
View Item |